Customized Single and double layer webbing manufactor Not only the production process is complex, but also the packaging process is very complicated. Only the webbing that has passed the inspection can be packaged out of the warehouse, otherwise it will be treated as defective products. Benxi Customized Single and double layer webbing manufactor The specific packaging process is as follows: 1. The process control method: 1. The surface of each winding tape must be smooth and flat (except for special webbing); Those who cannot be involved in substandard products shall be held accountable according to the seriousness of the case. Knot: ≤ 3/100Y, ≤ 2/50Y; Short code: ± 0.5/100Y; Each knapsack strap must have the label of the tape coiler. Inspection according to the customer's requirements: for example, 336, 217, 115, 314, 108, 114, 384, 206, 419, 122 adhesive paper and rubber hose, no pins can be used;
The application of is already very common, and the technology is also new one by one. Let's talk about it briefly from the manufacturer's editor. I hope it can help. It is well known that it has been widely used. Now many bag webbing manufacturers are constantly upgrading their products to make our life more convenient. Knitting can not only weave belts, but also weave ropes. Tubular belt is a kind of braided rope. Rope or rope with a diameter of 1~4 cm is also called rope. Rope with a diameter of more than 4 cm is also called rope. Rope with a diameter of more than 40 cm is generally called cable or rope.
The tensile strength after light treatment, the natural light shines on the bag webbing through the window, causing aging and reducing its strength. According to the working conditions, a lighting equipment is designed, which is equipped with representative strong light and is exposed to the light for a specified time. After lighting, pp webbing needs to be subjected to standard temperature and humidity treatment, and then to tensile test to obtain the tensile strength after lighting treatment. After soaking, the tensile strength of the safety belt installed in the car will absorb the moisture in the air, and sometimes it will be soaked by some liquid, so the immersion test is required. At room temperature, fully immerse in distilled water with a small amount of wetting agent for a specified time, and then take out the soaked pp webbing from the water to complete the tensile test within 10 minutes. The tensile strength of soaked pp webbing was obtained.
If the weft needle is damaged, replace it or beat it with gauze; If the steel buckle is damaged, hit it with gauze or replace the steel buckle; The coir filament piece is damaged or the shutdown piece is damaged. Replace it with a new one. Causes of poor needle edge: uneven weft yarn thickness; The knitting needle is not properly laid, too long or too short; The pan head moves abnormally, sometimes tight, sometimes loose; The weft wheel is not round enough and deformed; The fixing pin of knitting needle is worn; Precautions: change another weft yarn; The knitting needle is longer or shorter according to the thickness of the ribbon. Generally speaking, the length of the knitting needle is just enough to remove the weft; Fix both sides of the pan head firmly, and do not let the pan head lean against the iron frame on both sides; Replace the weft wheel with a new one; Replace the fixed rod or go to processing.
In the 1970s, due to the promotion of continuous ribbon dyeing and ironing machine, the processing of ribbon has developed from the traditional process of dyeing before weaving to weaving before dyeing, weaving before bleaching, ironing after processing, and the ribbon technology has entered the ranks of mechanized mass production. In the early 1980s, the industry introduced high-speed shuttleless loom, ironing machine, wrapping machine, warping machine, etc. from Switzerland, Italy and the Federal Republic of Germany, and the ribbon technology entered a new stage of development. The progress of webbing technology has brought about the upgrading of products. In 1980, the rubber ingot belt was developed, which has the characteristics of soft, light, thin, firm, small elongation, small impact force, short and flat joints.