The narrow Shenzhen ribbon or tubular fabric is made from various yarns. There are many kinds of belt fabrics, which are widely used in clothing, shoes, bags, industry, agriculture, military supplies, transportation and other industrial sectors. In the 1930s, it was all handmade workshops that produced exquisite pictures of ribbons. The raw materials were cotton thread and hemp thread. After the founding of the People's Republic of China, the raw materials for ribbon gradually developed to nylon, vinylon, polyester, polypropylene, spandex, viscose, etc., forming three major types of technology: weaving, knitting, knitting. The fabric structure includes plain weave, twill, satin, jacquard, double-layer, multi-layer, tubular and combined weave.
The convex and concave convex fabrics are compact and delicate on the front, with strip or pattern convex patterns, and rough on the back, with long floating lines. Wool fabric: single side woolen fabric, with the pile side being the front side of the fabric. For double-sided fleece fabric, the front side shall be the smooth and tidy side. Observe the selvage of the fabric: if the selvage is smooth, the neat side is the front side of the fabric. For double-layer, multi-layer and multiple fabrics, if the warp and weft density of the front and the back is different, the front side has a larger density or the front side has better raw materials.
One of the complete knowledge of printing types. There are many kinds of bag ribbon printing. Today, it is divided into two parts for everyone to talk about. If you like it, you can have a detailed look. It should be helpful to you. Here is the first part. Bag webbing transfer printing. The pigment is printed on the paper by printing method to make transfer printing paper, and then the color is transferred to the fabric by high temperature (heating and pressing on the back of the paper). It is generally used for chemical fiber fabrics, characterized by bright colors, fine layers, lifelike patterns, and strong artistry. However, this process is currently only applicable to a few synthetic fibers such as polyester. Transfer printing process is simple, investment is small and production is flexible. It is popular in the market at present But to be honest, compared with other types of printing, the price of this transfer printing is a little high, but it has a certain level.
But because Benxi Customized Webbing Manufacturer It has a certain hardness, so it is not suitable for large area of field patterns. Large area patterns should be printed with water slurry, and then dotted with glue slurry, which can not only solve the problem of large area of hard glue, but also highlight the sense of hierarchy of patterns; Another method is to steal a large area of field patterns and make them look bad, but they are always hard to wear. Therefore, it is better to combine water and glue to solve the problem of large area printing. Customized Webbing It has smooth surface and matte surface. It has soft, thin, environmental protection and other characteristics, and can be stretched. Generally speaking, glue printing is more commonly used. For leisure brands such as "Yichun", they basically use glue ¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡¡.
The tensile strength after light treatment, the natural light shines on the bag webbing through the window, causing aging and reducing its strength. According to the working conditions, a lighting equipment is designed, which is equipped with representative strong light and is exposed to the light for a specified time. After lighting, pp webbing needs to be subjected to standard temperature and humidity treatment, and then to tensile test to obtain the tensile strength after lighting treatment. After soaking, the tensile strength of the safety belt installed in the car will absorb the moisture in the air, and sometimes it will be soaked by some liquid, so the immersion test is required. At room temperature, fully immerse in distilled water with a small amount of wetting agent for a specified time, and then take out the soaked pp webbing from the water to complete the tensile test within 10 minutes. The tensile strength of soaked pp webbing was obtained.